1400トルコ青釉(M)(1.8L) new - Glaze cracking or shrinkage

- Glaze cracking or shrinkage <br>If dust

Q: What causes the pigment to crawl or repel during firing

try rubbing it with a towel

還元：1280℃   酸化：1230℃

and the only stone-milling technology in Japan to micro-pulverize the grains

1400トルコ青釉(M)(1.8L) new - Glaze cracking or shrinkage[Firing conditions for sample plates] Clay components <br>For porcelain: Amakusa Senchu (SiO2 72. 04% Al2O3 18. 16% Fe2O3 0. 65% TiO2 0. 04% CaO 0. 49% MgO 0. 09% Na2O 0. 58% K2O 3. 00% Ig. Loss 4. 55%) Firing temperature : Reduction: 1280 Glazing : Baume concentration 50 (soak for about 3 seconds) [How to use] Soil type: porcelain, pottery Possible firing method: oxidation and reduction possible Appropriate firing temperature: 1230 1300 Baume